【Overview】 Low VOCs content, two-component epoxy primer.
【Characteristics】 Good adhesion to substrates, excellent water resistance, rust prevention performance, and outstanding chemical resistance. A primer that can be used with both water-based and oil-based topcoats, with a wide range of applications.
【Composition】 Water-based epoxy resin, modified polyamide resin, pigments, additives, deionized water.
【Usage】 Suitable for metal surfaces such as steel, cast iron, and aluminum; for example: passenger cars, engineering machinery, agricultural machinery, vehicle chassis, automotive parts for axles, wind turbine towers, etc. Suitable for products that are paired with water-based acrylic topcoats in both dry and wet conditions.

【Construction Instructions】

This product is a two-component coating packaged in two barrels. It should be mixed according to the specified ratio before use. Once mixed, it must be used within the specified usable time.

(1) After opening the barrel, component A needs to be stirred evenly first; it is recommended to use a power mixer for stirring.

(2) Mix the curing agent (component B) and the main paint (component A) in the specified ratio using a mixer until uniform.

Paint solid ratio: 5:1 (by weight);

Dilution ratio: 0-15% (clean water)

Activation period after mixing:

Coating methods: airless spraying, air spraying, brushing, rolling. It is recommended to use airless or air spraying (with pressure tank). The thickness of a single spray should not be too thick; a wet film thickness of no more than 150μm is appropriate. Recoating can proceed once the previous coat has dried to touch.

Environmental requirements: Minimum application temperature: 5℃; Maximum application humidity: 80% R.H.

[Precautions] Do not allow paint to remain in paint pipes or spray guns or spraying equipment.

[Cleaning] Use alkaline clean water to thoroughly rinse all equipment.

[Compatibility]

[Original Paint Performance]

[Construction Performance]

【Workability】

【Paint film performance】